Made by sol-gel reaction of silica used in metal surface of the substrate for release film
| العنوان: | Made by sol-gel reaction of silica used in metal surface of the substrate for release film |
|---|---|
| العنوان البديل: | 以溶膠-凝膠反應製備二氧化矽應用於金屬基材表面離型薄膜之研究 |
| المؤلفون: | Chun-Yen Kuo, 郭俊彥 |
| مرشدي الرسالة: | 程耀毅 |
| سنة النشر: | 2013 |
| المجموعة: | National Digital Library of Theses and Dissertations in Taiwan |
| الوصف: | 101 Silica is a nanostructured, highly porous solid. that present properties, Silica has superior properties, such as, extremely low densities, low thermal conductivity and high surface area. The purpose of this study is to use sol-gel method to synthesize silica thin film and to compare the influence of the solvents using in this process. The result has indicated that the gelation time is greatly increased, when isopropanol / TEOS mole ratio greater than 2. Sol-gel thin film is formed on metal substrates by dip coating and drying in oven. Using couping agent to enhance the bonding between SiO2 film and metal substrates was studied. The properties of the prepared film were studied including thermal properties, morphology, planarity, thickness, and its dispersion, absorption, and harness. This study utilized many analytical instruments, including SEM, AFM, and contact angle measment tool. The SEM results, the particles size and surface structure were observed. The SEM images show that silica particle have diameter of nano meter scale. |
| Original Identifier: | 101TIT05310041 |
| نوع الوثيقة: | 學位論文 ; thesis |
| وصف الملف: | 82 |
| الإتاحة: | http://ndltd.ncl.edu.tw/handle/92s5rqTest |
| رقم الانضمام: | edsndl.TW.101TIT05310041 |
| قاعدة البيانات: | Networked Digital Library of Theses & Dissertations |
| الوصف غير متاح. |