Effect of Different Heat Treatment States on Chemical Milling Properties of 2195 Al-Li Alloy
العنوان: | Effect of Different Heat Treatment States on Chemical Milling Properties of 2195 Al-Li Alloy |
---|---|
المؤلفون: | XIAN Peng, FU Qiang, ZHENG Sen-mu, TANG Shuai, HUANG Peng-fei |
المصدر: | Cailiao Baohu, Vol 56, Iss 1, Pp 77-81 (2023) |
بيانات النشر: | Editorial Department of Materials Protection, 2023. |
سنة النشر: | 2023 |
المجموعة: | LCC:Materials of engineering and construction. Mechanics of materials LCC:Technology |
مصطلحات موضوعية: | 2195 al-li alloy, heat treatment state, chemical milling, surface quality, Materials of engineering and construction. Mechanics of materials, TA401-492, Technology |
الوصف: | For studying the effect of different heat treatment states on the chemical milling properties of 2195 Al-Li alloy, orthogonal experiments were used to research the chemical milling properties of 2195 Al-Li alloys with different heat treatment states(T8 state and O state) under different process parameters. Results showed that the chemical milling rate in T8 state was higher than that in O-state under different process parameters, and the side cutting rate in T8 state was more stable than that in O-state. Meanwhile, the surface quality of 2195 Al-Li alloy after chemical milling was related to the heat treatment state. The O-state sample had different degrees of etching grooves at the rib position after chemical milling, while the T8-state sample was smooth and flat and had better surface quality after chemical milling. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | Chinese |
تدمد: | 1001-1560 |
العلاقة: | http://www.mat-pro.com/fileup/1001-1560/PDF/230112.pdfTest; https://doaj.org/toc/1001-1560Test |
DOI: | 10.16577/j.issn.1001-1560.2023.0012 |
الوصول الحر: | https://doaj.org/article/61e321cc31f146ce9feca1e3d70da25bTest |
رقم الانضمام: | edsdoj.61e321cc31f146ce9feca1e3d70da25b |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 10011560 |
---|---|
DOI: | 10.16577/j.issn.1001-1560.2023.0012 |