Microwave-absorbing characteristics for the composites of thermal-plastic polyurethane (TPU)-bonded NiZn-ferrites prepared by combustion synthesis method
| العنوان: | Microwave-absorbing characteristics for the composites of thermal-plastic polyurethane (TPU)-bonded NiZn-ferrites prepared by combustion synthesis method |
|---|---|
| المؤلفون: | Peng, CH, Hwang, CC, Wan, J, Tsai, JS, Chen, SY |
| المساهمون: | 材料科學與工程學系, Department of Materials Science and Engineering |
| سنة النشر: | 2005 |
| المجموعة: | National Chiao Tung University: NCTU Institutional Repository / 國立交通大學機構典藏 |
| مصطلحات موضوعية: | NiZn ferrites, microwave absorbers, reflection loss, combustion synthesis |
| الوصف: | NiZn ferrite with the chemical formula Ni0.5-xZn0.5-xM2xFe2O4 (M = Co, Cu, or Mg, and x = 0 or 0.05) was synthesized by a combustion synthesis method using metal nitrates and urea ((NH2)(2)CO) as reactants. The narrocrystallite of these materials were mixed with a thermal-plastic polyurethane (TPU) elastomer to be converted into a microwave-absorbing composite. The complex relative permittivity (epsilon(r) = epsilon'-jepsilon") and permeability (mu(r)=mu'-jmu") of the absorber were measured in a frequency range of 2-12GHz. The reflection loss (R.L.), matching frequency (f(m)) and matching thickness (d(m)) were calculated using the theory of the absorbing wall. Effects of both the particle size of ferrite and the dopant presented in the ferrite on the electromagnetic properties and microwave-absorbing characteristics were investigated. It was found that nanoparticles around 40 nm exhibit higher reflection loss than both those obtained from micro-sized powders and those with size less than 25 nm. Also, it was shown that the Co-doped, Mg-doped, and Cu-doped NiZn ferrite-TPU composites could be designed to be more negative than -20 dB, in a frequency range of 2-12 GHz, to become promising materials for microwave-absorbing application. These doped ferrite-containing composites have more effective microwave-absorbing characteristics compared to undoped one. (C) 2004 Elsevier B.V. All rights reserved. |
| نوع الوثيقة: | article in journal/newspaper |
| اللغة: | English |
| تدمد: | 0921-5107 |
| العلاقة: | http://dx.doi.org/10.1016/j.mseb.2004.10.022Test; http://hdl.handle.net/11536/13996Test; MATERIALS SCIENCE AND ENGINEERING B-SOLID STATE MATERIALS FOR ADVANCED TECHNOLOGY |
| DOI: | 10.1016/j.mseb.2004.10.022 |
| الإتاحة: | https://doi.org/10.1016/j.mseb.2004.10.022Test http://hdl.handle.net/11536/13996Test |
| رقم الانضمام: | edsbas.9FE1D8CD |
| قاعدة البيانات: | BASE |
| تدمد: | 09215107 |
|---|---|
| DOI: | 10.1016/j.mseb.2004.10.022 |