التفاصيل البيبلوغرافية
| العنوان: |
The influence of aging on the fracture load of milled monolithic crowns |
| المؤلفون: |
Güleç, Ceyda, Sarıkaya, Işıl |
| المصدر: |
BMC Oral Health ; volume 22, issue 1 ; ISSN 1472-6831 |
| بيانات النشر: |
Springer Science and Business Media LLC |
| سنة النشر: |
2022 |
| مصطلحات موضوعية: |
General Dentistry |
| الوصف: |
Background This in-vitro study was conducted to assess the effect of aging on the fracture load of molar crowns fabricated with monolithic CAD/CAM materials. Methods The crown restorations were produced from Cerasmart, Vita Enamic, and IPS e.max CAD blocks. Aging was applied to the 10 samples each of monolithic CAD/CAM materials ( n = 10). Dual-axis chewing simulator (50 N, 1.1 Hz, lateral movement: 1 mm, mouth opening: 2 mm, 1,200,000 cycles) and thermocycling (± 5–55 °C, 6000 cycles) were applied as an aging procedure. 10 samples each of monolithic CAD/CAM materials without aging ( n = 10) were considered the control group. 6 tested groups were obtained. Then, all samples were evaluated in a universal testing machine to determine the fracture loading values’. Results There was not a statistically significant difference between the fracture load values before and after aging for all samples of Cerasmart, Vita Enamic, and IPS e.max CAD ( p > 0.005). In a comparison of the monolithic materials together, a statistically significant difference was found between the fracture load values of IPS e.max CAD and Vita Enamic crowns before aging ( p = 0.02). Also, Vita Enamic crowns (1978,71 ± 364,05 N) were found different from the IPS e.max CAD ( p = 0.005) and Cerasmart crowns ( p = 0.041) after aging. Conclusions Dynamic aging with 1.200.000 cycles was found to have no effect to fracture loading on milled Cerasmart, Vita Enamic, and IPS e.max CAD monolithic crowns. |
| نوع الوثيقة: |
article in journal/newspaper |
| اللغة: |
English |
| DOI: |
10.1186/s12903-022-02529-z |
| DOI: |
10.1186/s12903-022-02529-z.pdf |
| DOI: |
10.1186/s12903-022-02529-z/fulltext.html |
| الإتاحة: |
https://doi.org/10.1186/s12903-022-02529-zTest |
| حقوق: |
https://creativecommons.org/licenses/by/4.0Test ; https://creativecommons.org/licenses/by/4.0Test |
| رقم الانضمام: |
edsbas.6621AC03 |
| قاعدة البيانات: |
BASE |