On the Degradation of Retained Austenite in Transformation Induced Plasticity Steel
العنوان: | On the Degradation of Retained Austenite in Transformation Induced Plasticity Steel |
---|---|
المؤلفون: | Peter Hodgson, Ilana Timokhina, Frank Niessen, Azdiar A. Gazder, Ilias Bikmukhametov, Jiangting Wang, Elena V. Pereloma |
المصدر: | Metallurgical and Materials Transactions A. 51:3802-3810 |
بيانات النشر: | Springer Science and Business Media LLC, 2020. |
سنة النشر: | 2020 |
مصطلحات موضوعية: | 010302 applied physics, Austenite, Materials science, Bainite, Metallurgy, 0211 other engineering and technologies, Metals and Alloys, 02 engineering and technology, Plasticity, Condensed Matter Physics, 01 natural sciences, Isothermal transformation diagram, Mechanics of Materials, Martensite, 0103 physical sciences, Substructure, Thermomechanical processing, Pearlite, 021102 mining & metallurgy |
الوصف: | A transformation-induced plasticity steel was thermomechanically processed and then transformed to bainite at an isothermal transformation temperature of 723 K for 1800 seconds, which exceeds the time required for completion of the bainite transformation. The formation of lenticular-shaped carbides with a triclinic lattice and internal substructure was found after thermomechanical processing. After 16 years of storage at room temperature, the decomposition of retained austenite into pearlite was observed for the first time at this temperature. |
تدمد: | 1543-1940 1073-5623 |
الوصول الحر: | https://explore.openaire.eu/search/publication?articleId=doi_________::e7c7a47826cdc5c02bf6444c945479a4Test https://doi.org/10.1007/s11661-020-05823-zTest |
حقوق: | OPEN |
رقم الانضمام: | edsair.doi...........e7c7a47826cdc5c02bf6444c945479a4 |
قاعدة البيانات: | OpenAIRE |
تدمد: | 15431940 10735623 |
---|