Effect of MWCNT filled epoxy adhesives on the quality of adhesively bonded joints
| العنوان: | Effect of MWCNT filled epoxy adhesives on the quality of adhesively bonded joints |
|---|---|
| المؤلفون: | G Kotsikos, Maria Konstantakopoulou |
| المصدر: | Plastics, Rubber and Composites. 45:166-172 |
| بيانات النشر: | Informa UK Limited, 2016. |
| سنة النشر: | 2016 |
| مصطلحات موضوعية: | Materials science, Polymers and Plastics, General Chemical Engineering, Glass fiber, chemistry.chemical_element, 02 engineering and technology, Epoxy, Fibre-reinforced plastic, 010402 general chemistry, 021001 nanoscience & nanotechnology, 01 natural sciences, 0104 chemical sciences, Lap joint, chemistry, Aluminium, visual_art, Materials Chemistry, Ceramics and Composites, Aluminium alloy, visual_art.visual_art_medium, Surface modification, Adhesive, Composite material, 0210 nano-technology |
| الوصف: | Most adhesively bonded joints exhibit adhesive or cohesive failure, i.e. failure at the adhesive/adherend interface or within the adhesive, respectively. The main objective of this study is to investigate the effect of surface modification of the metal substrate accompanied by modification of the adhesive properties on the strength and failure mechanism of bonded joints. A 5061 aluminium alloy has been used as the metal substrate onto which two types of surface treatments were applied; chemical surface modification and gritblasting. A standard epoxy resin was used as the adhesive medium, in which multi-wall carbon nanotubes (MWCNTs) were dispersed, with a range of weight fraction content (from 0.03% to 0.5%). The resin was fully characterised by mechanical testing in order to determine the optimum weight fraction to enhance its properties. Aluminium to aluminium and glass fibre reinforced polymer (GFRP) composite to aluminium single lap joints bonded with either pure epoxy resin or MWCNT reinforced epoxy ... |
| تدمد: | 1743-2898 1465-8011 |
| الوصول الحر: | https://explore.openaire.eu/search/publication?articleId=doi_________::b3b3d857735abddd9c1cadfef7510bd9Test https://doi.org/10.1080/14658011.2016.1165788Test |
| رقم الانضمام: | edsair.doi...........b3b3d857735abddd9c1cadfef7510bd9 |
| قاعدة البيانات: | OpenAIRE |
| تدمد: | 17432898 14658011 |
|---|