Morphology, structure, optical, and electrical properties of AgSbO3. |
| المؤلفون: |
Yi, Z. G., Liu, Y., Withers, R. L. |
| المصدر: |
Journal of Applied Physics; Aug2010, Vol. 108 Issue 2, p024911, 7p, 1 Black and White Photograph, 1 Diagram, 9 Graphs |
| مصطلحات موضوعية: |
SILVER, ANTIMONY, OXIDES, OPTICAL properties, NANOPARTICLES |
| مستخلص: |
The morphology of defect pyrochlore-type, AgSbO3 microparticle/nanoparticles obtained via solid state reaction evolve from irregular to Fullerene-like polyhedra before finally decomposing into metal-organic framework-5 like particles with increase in sintering temperature. The defect pyrochlore-type AgSbO3 particles are slightly Ag deficient while the valence of the antimony ion is shown to be +5 giving rise to a probable stoichiometry of Ag1-xSbVO3-x/2, with x∼0.01–0.04. A highly structured diffuse intensity distribution observed via electron diffraction is interpreted in terms of correlated displacements of one-dimensional (1D) silver ion chains along <110> directions. A redshifting in the absorption edges in UV-visible absorption spectra is observed for samples prepared at sintering temperatures higher than 1000 °C and attributed to the surface plasma resonance effect associated with small amounts of excess metallic Ag on the Ag1-xSbVO3-x/2 particles. An electrical properties investigation of the silver antimonate samples via dielectric, conductivity, and electric modulus spectroscopy shows a prominent dielectric relaxation associated with grain boundaries. The silver ion conductivity is associated with correlated displacements of 1D silver ion chains along <110> directions. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |