التفاصيل البيبلوغرافية
| العنوان: |
Large-scale micromagnetic simulation of Nd-Fe-B sintered magnets with Dy-rich shell structures. |
| المؤلفون: |
Oikawa, T., Yokota, H., Ohkubo, T., Hono, K. |
| المصدر: |
AIP Advances; 2016, Vol. 6 Issue 5, p1-6, 6p |
| مصطلحات موضوعية: |
MICROMAGNETICS, NEODYMIUM compounds, SINTERING |
| مستخلص: |
Large-scale micromagnetic simulations have been performed using the energy minimization method on a model with structural features similar to those of Dy grain boundary diffusion (GBD)-processed sintered magnets. Coercivity increases as a linear function of the anisotropy field of the Dy-rich shell, which is independent of Dy composition in the core as long as the shell thickness is greater than about 15 nm. This result shows that the Dy contained in the initial sintered magnets prior to the GBD process is not essential for enhancing coercivity. Magnetization reversal patterns indicate that coercivity is strongly influenced by domain wall pinning at the grain boundary. This observation is found to be consistent with the one-dimensional pinning theory. [ABSTRACT FROM AUTHOR] |
|
Copyright of AIP Advances is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |
Full Text Finder