العنوان: |
High-speed deposition of RE123 film with large current capacity by hot-wall type PLD system |
المؤلفون: |
Igarashi, M. m_igarashi@fujikura.co.jp, Kakimoto, K.1, Hayashida, T.1, Hanada, Y.1, Fujita, S.1, Morita, K.1, Nakamura, N.1, Hanyu, S.1, Sutoh, Y.1, Kutami, H.1, Iijima, Y.1, Saitoh, T.1 |
المصدر: |
Physica C. Nov2010, Vol. 470 Issue 20, p1230-1233. 4p. |
مصطلحات موضوعية: |
*PULSED laser deposition, *CRITICAL currents, *ELECTRIC heating, *COPPER oxide superconductors, *MICROFABRICATION, *THICKNESS measurement, *TEMPERATURE effect |
مستخلص: |
Abstract: We have studied a hot-wall heating system to produce GdBa2Cu3O y (GdBCO) films with large critical currents (I c) at a high production rate by a pulsed-laser-deposition (PLD) method. GdBCO films fabricated at a production rate of 30m/h under the optimized conditions, especially a distance of 95mm between the target and the substrate (T–S), exhibited high critical current densities (J c) of about 3MA/cm2 and I c over 300A at a thickness of 1–2μm. Furthermore, long GdBCO tapes prepared by repeated depositions at each tape-passing speed of 80m/h showed uniform I c distribution along the longitudinal direction, because the hot-wall system enabled to stabilize temperature within a few degrees at 800°C. A 170m long tape with I c over 600A was successfully fabricated at a production rate of 16m/h using a laser power of 360W. [ABSTRACT FROM AUTHOR] |