Effect of fabrication parameters on the ferroelectricity of hafnium zirconium oxide films: A statistical study. |
| المؤلفون: |
Salcedo, Guillermo A., Islam, Ahmad E., Reichley, Elizabeth, Dietz, Michael, Schubert-Kabban, Christine M., Leedy, Kevin D., Back, Tyson C., Wang, Weisong, Green, Andrew, Wolfe, Timothy, Sattler, James M. |
| المصدر: |
Journal of Applied Physics; 3/28/2024, Vol. 135 Issue 12, p1-8, 8p |
| مصطلحات موضوعية: |
HAFNIUM oxide films, FERROELECTRICITY, HYDROFLUORIC acid, ZIRCONIUM oxide, HAFNIUM oxide |
| مستخلص: |
Ferroelectricity in hafnium zirconium oxide (Hf1 − xZrxO2) and the factors that impact it have been a popular research topic since its discovery in 2011. Although the general trends are known, the interactions between fabrication parameters and their effect on the ferroelectricity of Hf1 − xZrxO2 require further investigation. In this paper, we present a statistical study and a model that relates Zr concentration (x), film thickness (tf), and annealing temperature (Ta) with the remanent polarization (Pr) in tungsten (W)-capped Hf1 − xZrxO2. This work involved the fabrication and characterization of 36 samples containing multiple sets of metal-ferroelectric-metal capacitors while varying x (0.26, 0.48, and 0.57), tf (10 and 19 nm), and Ta (300, 400, 500, and 600 ° C). In addition to the well-understood effects of x and Ta on the ferroelectricity of Hf1 − xZrxO2, the statistical analysis showed that thicker Hf1 − xZrxO2 films or films with higher x require lower Ta to crystallize and demonstrated that there is no statistical difference between samples annealed to 500 and 600 ° C, thus suggesting that most films fully crystallize with Ta ∼ 500 ° C for 60 s. Our model explains 95% of the variability in the Pr data for the films fabricated, presents the estimates of the phase composition of the film, and provides a starting point for selecting fabrication parameters when a specific Pr is desired. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Applied Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |