Preparation and properties of nano-calcium carbonate/styrene-butadiene-styrene block copolymer composite modified asphalt
العنوان: | Preparation and properties of nano-calcium carbonate/styrene-butadiene-styrene block copolymer composite modified asphalt |
---|---|
المؤلفون: | WANG Peng-fei, LI Wen-xia, SUN Ji-shu |
المصدر: | Hecheng xiangjiao gongye, Vol 45, Iss 4, Pp 320-325 (2022) |
بيانات النشر: | Editorial Office of China Synthetic Rubber Industry, 2022. |
سنة النشر: | 2022 |
المجموعة: | LCC:Organic chemistry LCC:Chemical engineering LCC:Chemicals: Manufacture, use, etc. |
مصطلحات موضوعية: | nano-calcium carbonate, styrene-butadiene-styrene block copolymer, composite modified asphalt, high and low temperature property, storage stability, Organic chemistry, QD241-441, Chemical engineering, TP155-156, Chemicals: Manufacture, use, etc., TP200-248 |
الوصف: | Nano-CaCO3 and styrene-butadiene-styrene block copolymer (SBS) were used as additives to prepare nano-CaCO3/SBS composite modified asphalt. The optimum amount of admixture was determined by testing basic physical properties, the performance and micro morphology of asphalt were investigated by rheological property and segregation test, fluorescence microscope observation and thermogravimetric analysis. The results showed that the best proportion of the two admixtures was 5% (mass fraction, the same below) of nano-CaCO3 and 4% of SBS. After adding SBS into nano-CaCO3 modified asphalt, the viscosity of the composite modified asphalt increased at different temperatures, high temperature rutting resistance and low-temperature performance was significantly improved, and storage stability was good. Nano-CaCO3 molecule, SBS molecule and matrix asphalt molecule had good compatibility, and the thermal stability of asphalt was enhanced because of the composite modification. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | Chinese |
تدمد: | 1000-1255 |
العلاقة: | http://hcxjgy.paperopen.com/oa/DArticle.aspx?type=view&id=202204011Test; https://doaj.org/toc/1000-1255Test |
DOI: | 10.19908/j.cnki.ISSN1000-1255.2022.04.0320 |
الوصول الحر: | https://doaj.org/article/aff1c23a9e5d4f3d826de653420f5f5aTest |
رقم الانضمام: | edsdoj.ff1c23a9e5d4f3d826de653420f5f5a |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 10001255 |
---|---|
DOI: | 10.19908/j.cnki.ISSN1000-1255.2022.04.0320 |