التفاصيل البيبلوغرافية
| العنوان: |
Characterization of nearly stoichiometric SiC ceramic fibres. |
| المؤلفون: |
Dong, S. M., Chollon, G., Labrugère, C., Lahaye, M., Guette, A., Bruneel, J. L., Couzi, M., Naslain, R., Jiang, D. L. |
| المصدر: |
Journal of Materials Science; May2001, Vol. 36 Issue 10, p2371-2381, 11p |
| مصطلحات موضوعية: |
SILICON, CARBON, CERAMIC fibers, MICROSTRUCTURE, STOICHIOMETRY |
| مستخلص: |
A comparative study of the chemical composition and microstructure of Hi-Nicalon, Hi-Nicalon type S, Tyranno SA, Sylramic and Carborundum fibres has been conducted. This analysis has confirmed results already published but has also evidenced some original features. The Hi-Nicalon type S fibre has a near stoichiometric composition but it still contains some oxygen (≈1 at. %) and free carbon (≈2 at. %). The expected near stoichiometric composition of both the Tyranno SA and the Sylramic fibres is only effective near the edge region, while the core of the fibres contains some amount of free carbon (e.g., up to ≈14 at. % and ≈6 at. % respectively in large diameter fibres) as well as some residual oxygen (≈0.5 at. %). The composition of the Carborundum fibre is very close to stoichiometric SiC except rare and localised free carbon or B4C inclusions. The properties of the different fibres, some of them still beeing at a development stage, are discussed from a chemical and a phase composition point of view, on the basis of what is known about their respective preparation process. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Materials Science is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Complementary Index |