THE INVESTIGATION OF POLYLACTIC ACID BASED NATURAL FIBER REINFORCED BIOCOMPOSITES FOR AUTOMOTIVE APPLICATIONS
العنوان: | THE INVESTIGATION OF POLYLACTIC ACID BASED NATURAL FIBER REINFORCED BIOCOMPOSITES FOR AUTOMOTIVE APPLICATIONS |
---|---|
المؤلفون: | ÖZTÜRK, Sinan |
المصدر: | Volume: 6, Issue: 1 21-31 ; 2458-7494 ; 2458-7613 ; Kırklareli Üniversitesi Mühendislik ve Fen Bilimleri Dergisi |
بيانات النشر: | Kırklareli Üniversitesi Kirklareli University |
سنة النشر: | 2020 |
المجموعة: | DergiPark Akademik (E-Journals) |
مصطلحات موضوعية: | Bio-based PLA polymer,Hemp natural fiber,Biocomposite,Automotive application |
الوصف: | An automotive application with renewablesources as environmentally sustainable solution has been studied for weightreduction. Hemp as non-woven natural fiber (NNF) and Polylactic acid (PLA)non-woven fibers has been used to form continuous mat by needle-punch method.This biobased mat structure was then hot formed to achieve good mechanicalproperties. The composition of the fiber was 50:50 / NNF:PLA and the density ofthe final sheet was 1300 gr/m2, the final thickness of thebiocomposite after themoforming was 2.2 mm with 2.1 GPa Flexural Modulus and 17MPa Tensile Strength and 2.3% elongation at break. In this study, themechanical performance of this biocomposite structure under water immersion,40ºC and 80ºC was studied. The charpy impact strength was found 21kJ/m2.The major outcome of this study is replacing conventional reinforcementmaterials with renewable sources which offers lower weight and tolerablemechanical strengths. |
نوع الوثيقة: | article in journal/newspaper |
وصف الملف: | application/pdf |
اللغة: | English |
العلاقة: | https://dergipark.org.tr/tr/download/article-file/1180934Test; https://dergipark.org.tr/tr/pub/klujes/issue/55707/626590Test |
DOI: | 10.34186/klujes.626590 |
الإتاحة: | https://doi.org/10.34186/klujes.626590Test https://dergipark.org.tr/tr/pub/klujes/issue/55707/626590Test |
رقم الانضمام: | edsbas.1BF23A7F |
قاعدة البيانات: | BASE |
DOI: | 10.34186/klujes.626590 |
---|