Optimization of tensile strength for new type acetone-urea-formaldehyde furan resin using uniform design
العنوان: | Optimization of tensile strength for new type acetone-urea-formaldehyde furan resin using uniform design |
---|---|
المؤلفون: | Lin Shengjun, Zhao Ya, Li Yuancai |
المصدر: | China Foundry, Vol 8, Iss 1, Pp 30-35 (2011) |
بيانات النشر: | Foundry Journal Agency, 2011. |
سنة النشر: | 2011 |
المجموعة: | LCC:Technology LCC:Manufactures |
مصطلحات موضوعية: | acetone-urea-formaldehyde furan resin, 24 h tensile strength, single factor experiment, uniform design, stepwise regression, Technology, Manufactures, TS1-2301 |
الوصف: | In this study, the 24 h tensile strength of new type acetone-urea-formaldehyde furan resin (nitrogen content 3%) was investigated by uniform design optimization. Four independent variables such as acetone : formaldehyde molar ratio (mol/mol), solution pH value, reaction temperature (℃) and reaction time (min) were considered in the experiments. U*13(134) uniform design was employed and the equation of 24 h tensile strength model was obtained after 13 experimentations. The 24 h tensile strength was optimized by applying single factor experiments and stepwise non-linear regression analysis. Minitab (Minitab 15 trial version) and MATLAB (R2010a trial version) were used for data analysis. The t-value and p-value indicate that the major impact factors include the interaction effect of solution pH value and reaction temperature (X2X3), the linear terms of acetone : formaldehyde molar ratio (X1), reaction time (X4) followed by the square effects of acetone/formaldehyde molar ratio (X1X1). The optimized results were achieved with the acetone: formaldehyde molar ratio (mol/mol) at 3:1, solution pH value at 6.0, reaction temperature at 70 ℃, and reaction time at 140 min, respectively. This method can not only significantly reduce the number and cost of the tests, but also provide a good experimental design strategy for the development of furan resin. The investigation shows that the predicted results of 24 h tensile strength are consistent well with the experimental ones. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1672-6421 |
العلاقة: | http://www.foundryworld.com/uploadfile/201131448454541.pdfTest; https://doaj.org/toc/1672-6421Test |
الوصول الحر: | https://doaj.org/article/7a9327bf079043259ea4fcf3108e2813Test |
رقم الانضمام: | edsdoj.7a9327bf079043259ea4fcf3108e2813 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 16726421 |
---|