| العنوان: |
高密度重组竹的物理力学性能研究. |
| العنوان البديل: |
Study on The Physical and Mechanical Properties of High-Density Bamboo Scrimbers. |
| المؤلفون: |
许 杨1, 刘 倩1, 孙子健1, 魏金光2, 于文吉3 weijorn@163.com |
| المصدر: |
China Forest Products Industry. Jun2024, Vol. 61 Issue 6, p20-26. 7p. |
| الملخص (بالإنجليزية): |
Bamboo scrimber with high density was studied to reveal the influence of density on the physical and mechanical properties by analyzing the porosity and microstructure, water resistance and mechanical properties and establishing the quantitative relationships between the density and as-resulted metrics. The results showed that the porosity declined with an increase in density. Bamboo cells were densified at 1.37 g/cm3 and the porosity was 5.52%. Parenchyma cells and vessel cells were severely deformed, while fibrous cells were invariable. The water absorption, thickness swelling, and width swelling decreased with the increasing density after the scrimbers were treated in boiling water for 4 hours, in an oven at 63 C for 20 hours and in boiling water for additional 4 hours, and their lowest values were 9.67%, 7.62%, and 1.47%, respectively. The horizontal shear strength, parallel-to-grain compressive strength, MOR, and MOE increased with the density, and their maximum values were 28.83, 215.53, 354.00 MPa, and 28.75 GPa, respectively. The performance metrics of all the tested scrimbers met the outdoor bamboo scrimbers' requirements, and some far exceeded the highest level specified in national standards. The results can provide theoretical and data references for the performance regulation and application of bamboo scrimbers. [ABSTRACT FROM AUTHOR] |
| Abstract (Chinese): |
分析了高密度重组竹的孔隙率、微观结构、耐水性和力学性能, 并通过构建性能参数与密度的关系, 探究密度对物理力 学性能的影响规律。结果表明:随着密度的增大, 孔隙率逐渐降低。当密度为1.37 g/cm3时, 孔隙率仅为5.52%,竹材细胞基本实 现了密实化;薄壁细胞和导管细胞发生严重变形, 但纤维细胞的形态几乎未受影响。经4 h水煮-20 h 60 °C干燥-4 h水煮处理 后, 吸水率、厚度膨胀率和宽度膨胀率均随密度的增大而下降, 分别低至9.67%、7.62%和1.47%。水平剪切强度、顺纹抗压强度、 静曲强度(MOR)和弹性模量(MOE)」随密度的增大而增大, 分别高达28.83、215.53、354.00 MPa和28.75 GPa。所有重组竹的 性能参数均达到了户外用重组竹的性能要求, 且部分参数远超国标中规定的最高等级要求。此研究结果可为重组竹性能的调 控与应用提供理论依据和数据参考. [ABSTRACT FROM AUTHOR] |
|
Copyright of China Forest Products Industry is the property of China Forest Products Industry Editorial Office and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |
| قاعدة البيانات: |
Business Source Index |