التفاصيل البيبلوغرافية
| العنوان: |
Fundamental material property trends in the La0.8-xNdxCa0.2FeO3-δ series: crystal structure and thermal expansion. |
| المؤلفون: |
Berger, Christian, Bucher, Edith, Lammer, Judith, Nader, Christina, Sitte, Werner |
| المصدر: |
Journal of Materials Science; 2021, Vol. 56 Issue 17, p10191-10203, 13p, 1 Color Photograph, 2 Diagrams, 5 Charts, 4 Graphs |
| مصطلحات موضوعية: |
THERMAL expansion, SCANNING transmission electron microscopy, CRYSTAL structure, MECHANICAL properties of condensed matter, RIETVELD refinement |
| مستخلص: |
Compounds from the series La0.8-xNdxCa0.2FeO3-δ (0.1 ≤ x ≤ 0.7) were synthesised by a sol–gel route. X-ray diffraction and Rietveld analysis showed that materials with 0 ≤ x ≤ 0.6 crystallize as single-phase orthorhombic perovskites. The smaller ionic radius of Nd3+ compared to La3+ leads to a decrease in unit cell volume with increasing x. Elemental mapping by high-resolution scanning transmission electron microscopy with energy-dispersive X-ray spectroscopy confirms the homogeneous distribution of the A-site elements (La, Nd and Ca) in the perovskite (ABO3) lattice. The thermal expansion behaviour of La0.8-xNdxCa0.2FeO3-δ (0 ≤ x ≤ 0.6) was characterized by dilatometry at 30 ≤ T/°C ≤ 1000 and 1 × 10–3 ≤ pO2/bar ≤ 1. The thermal expansion coefficients of La0.8-xNdxCa0.2FeO3-δ, which were determined in regions I (40–530 °C) and II (530–990 °C), respectively, are almost independent of the Nd concentration in the range of (0 ≤ x ≤ 0.6) and increase slightly with decreasing pO2. The transition from orthorhombic to trigonal modification, which is observed for La0.8Ca0.2FeO3-δ at approx. 740 °C, is suppressed for all Nd-substituted compounds with x ≥ 0.1. [ABSTRACT FROM AUTHOR] |
|
Copyright of Journal of Materials Science is the property of Springer Nature and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.) |