Thermal and mechanical properties of modified CaCO3 filled poly (ethylene terephthalate) nanocomposites
العنوان: | Thermal and mechanical properties of modified CaCO3 filled poly (ethylene terephthalate) nanocomposites |
---|---|
المؤلفون: | Hong-Un Kim, Lee Changsoo, Kwan Han Yoon, Young-Bin Park, Jae Cheol Park |
المصدر: | Fibers and Polymers. 15:1493-1499 |
بيانات النشر: | Springer Science and Business Media LLC, 2014. |
سنة النشر: | 2014 |
مصطلحات موضوعية: | Materials science, Ethylene, Morphology (linguistics), Nanocomposite, food.ingredient, Polymers and Plastics, General Chemical Engineering, General Chemistry, Dynamic mechanical analysis, Sodium oxalate, chemistry.chemical_compound, food, chemistry, Ultimate tensile strength, Composite material, Glass transition, Filler (animal food) |
الوصف: | Poly(ethylene terephthalate) (PET)/CaCO3 and PET/modified-CaCO3 (m-CaCO3) nanocomposites were prepared by melt blending. The morphology indicated that m-CaCO3 produced by reacting sodium oxalate and calcium chloride, was well dispersed in PET matrix and showed good interfacial interaction with PET compared to CaCO3. No significant differences in the thermal properties such as, glass transition, melting and degradation temperatures, of the nanocomposites were observed. The thermal shrinkage of PET at 120 °C was 10.8 %, while those of PET/CaCO3 and PET/m-CaCO3 nanocomposites were 2.9–5.2 % and 1.2–2.8 %, respectively depending on filler content. The tensile strength of PET/CaCO3 nanocomposite decreased with CaCO3 loading, whereas that of PET/m-CaCO3 nanocomposites at 0.5 wt% loading showed a 17 % improvement as compared to neat PET. The storage modulus at 120 °C increased from 1660 MPa for PET to 2350 MPa for PET/CaCO3 nanocomposite at 3 wt% loading, and 3230 MPa for PET/m-CaCO3 nanocomposite at 1 wt% loading. |
تدمد: | 1875-0052 1229-9197 |
الوصول الحر: | https://explore.openaire.eu/search/publication?articleId=doi_________::d8c5c6e7705e52166354eefc1656f157Test https://doi.org/10.1007/s12221-014-1493-0Test |
حقوق: | CLOSED |
رقم الانضمام: | edsair.doi...........d8c5c6e7705e52166354eefc1656f157 |
قاعدة البيانات: | OpenAIRE |
تدمد: | 18750052 12299197 |
---|