Development and studies on the influence of the application and polymerization processes of an acrylates UV-cured clear-coat (high solid content) ; Développement et études de l’influence des procédés d’application et de réticulation de vernis acrylates photo-polymérisables (à 100% d’extrait sec)
| العنوان: | Development and studies on the influence of the application and polymerization processes of an acrylates UV-cured clear-coat (high solid content) ; Développement et études de l’influence des procédés d’application et de réticulation de vernis acrylates photo-polymérisables (à 100% d’extrait sec) |
|---|---|
| المؤلفون: | Laurent, Sabine |
| المساهمون: | Ingénierie des Matériaux Polymères (IMP), Université Claude Bernard Lyon 1 (UCBL), Université de Lyon-Université de Lyon-Institut National des Sciences Appliquées de Lyon (INSA Lyon), Université de Lyon-Institut National des Sciences Appliquées (INSA)-Institut National des Sciences Appliquées (INSA)-Université Jean Monnet - Saint-Étienne (UJM)-Institut de Chimie - CNRS Chimie (INC-CNRS)-Centre National de la Recherche Scientifique (CNRS), INSA de Lyon, Jean-Yves Charmeau |
| المصدر: | https://theses.hal.science/tel-01127623Test ; Matériaux. INSA de Lyon, 2014. Français. ⟨NNT : 2014ISAL0006⟩. |
| بيانات النشر: | HAL CCSD |
| سنة النشر: | 2014 |
| المجموعة: | HAL Lyon 1 (University Claude Bernard Lyon 1) |
| مصطلحات موضوعية: | Varnish, Polyurethane acrylate coating, Scratch strenght, Coating proccess impact, Crosslinking impact, Photopolymerization, Polycarbonate, Microscratch test, UV radiation, High solid content, UV energy, Irradiance peak, Vernis, Revêtement polyuréthane acrylate, Résistance à la rayure, Impact du procédé d'application, Impact de la réticulation, Photopolymérisation, Test Microscratch, Rayonnement UV, Haute teneur en extrait sec, Dose UV, Pic d'irradiance, [SPI.MAT]Engineering Sciences [physics]/Materials |
| الوصف: | This research aimed to study the impact of the application and the curing process conditions on the UV-cured coating properties. The UV formulation is a high solid content clear-coat, containing acrylates oligomer and monomers, and developed for thermoplastics substrate, to protect them against scratches. The characterization of the coating and the polycarbonate substrate showed the interaction between the two polymers. UV irradiation is the key to create the polymer network. Several parameters can affect the evolution of its energy and intensity: the conveyor speed, the position of the sample under the bulb, the distance between the last two, and the focalisation of the UV rays. The coating is then analysed in terms of scratch resistance, by the microscratch test. This test gives information about the ductile/brittle transition, the elastic behaviour and the adhesion work. It is completed by the reticulation rate measure. These properties can be modified by the UV radiation setting and the process conditions, like the angle of the support, the coating thickness, and the thermic pre-treatment of the materials before the application or the curing. The clear coat is aimed to be sprayed by electrostatic rotary deposition. The study of the rheological behaviour of the liquid coating showed an impact of the heating on its viscosity. Semi-industrials tests allowed highlighting the process parameters in order to improve the coating levelling and appearance. ; Le travail présenté porte sur l’étude de la résistance à la rayure d’un vernis acrylate liquide à 100% d’extrait sec et photo-réticulable, en fonction des conditions de réticulation et d’application. Ce vernis est destiné à être appliqué sur des substrats thermoplastiques. Une première étude réalisée sur support polycarbonate a permis de mettre en évidence l’interaction entre le supporte et les monomères du vernis. La photo-polymérisation nécessite une source de rayonnement UV afin de former le réseau 3D. L’évolution de l’énergie (dose UV) et de la puissance (pic ... |
| نوع الوثيقة: | doctoral or postdoctoral thesis |
| اللغة: | French |
| العلاقة: | NNT: 2014ISAL0006; tel-01127623; https://theses.hal.science/tel-01127623Test; https://theses.hal.science/tel-01127623/documentTest; https://theses.hal.science/tel-01127623/file/2014ISAL0006.pdfTest |
| الإتاحة: | https://theses.hal.science/tel-01127623Test https://theses.hal.science/tel-01127623/documentTest https://theses.hal.science/tel-01127623/file/2014ISAL0006.pdfTest |
| حقوق: | info:eu-repo/semantics/OpenAccess |
| رقم الانضمام: | edsbas.8970E976 |
| قاعدة البيانات: | BASE |
| الوصف غير متاح. |